Dam Liner (hdpe liner geomembrane for dam liners)

Dam Liner (hdpe liner geomembrane for dam liners) has the advantages of high anti-seepage performance, good durability, convenient and quick construction, economical and practical, and can effectively ensure the safety and stability of the dam. Geomembrane is widely used in dam engineering. It plays an important role in anti-seepage layer, anti-leakage layer and protective layer.

Classification :

Dam Liner

Keywords :

Dam Liner

+8615806698096

info@sdzhgeomaterials.com

E-mail

PRODUCT DETAILS

Construction technology

Geomembrane paving is completed, should minimize walking on the membrane surface, moving tools, etc., where the geomembrane can cause harm to the object, should not be placed on the membrane or carry walking on the membrane, so as not to cause accidental damage to the membrane. When laying geomembrane, we should strive to weld less, under the premise of ensuring the quality of welding, and try to save raw materials. The lap width of the joints between the membrane and the membrane is generally not less than 10cm, and the weld seams are usually arranged parallel to the larger slope, i.e. along the direction of the slope.

Technical indicators

Ordinary high-density polyethylene geomembrane (GB/T 17643 2011 GH-1 type technical indicators)

Item	Indicator
Thickness m m	0.30	0.50	0.75	1.00	1.25	1.50	2.00	2.50	3.00
densities g/cm³	≥0.940
Tensile yield strength (longitudinal and transverse) N/mm	≥4	≥7	≥10	≥13	≥16	≥20	≥26	≥33	≥40
Tensile breaking strength (longitudinal and transverse) N/mm	≥6	≥10	≥15	≥20	≥25	≥30	≥40	≥50	≥60
Yield elongation (longitudinal and transverse) %				≥11
Elongation at break (longitudinal and transverse) %	≥600
Right angle tearing load (longitudinal and transverse) N	≥34	≥56	≥84	≥115	≥140	≥170	≥225	≥280	≥340
Puncture strength N	≥72	≥120	≥180	≥240	≥300	≥360	≥480	≥600	≥720
Carbon black content %	2.0-3.0
Carbon Black Dispersibility	No more than 1 out of 10 data at level 3, not allowed at levels 4 and 5
Atmospheric pressure oxidation induction time (OIT)min	≥60
Low temperature impact embrittlement properties	pass
water vapor permeability coefficient g ·cm/(cm2 · s ·Pa)	≤1.0×10-13
Dimensional stability %	±2.0

Environmental protection high-density polyethylene geomembrane "GB/T 17643-2011 GH-2S type technical indexes

Item	Indicator
thicknesses mm	0.75	1.00	1.25	1.50	2.00	2.50	3.00
Densities g/cm³	≥0.940
Tensile yield strength (longitudinal and transverse) N/mm	≥11	≥15	≥18	≥22	≥29	≥37	≥44
Tensile breaking strength (longitudinal and transverse) N/mm	≥20	≥27	≥33	≥40	≥53	≥67	≥80
Yield elongation (longitudinal and transverse) %	≥12
Elongation at break (longitudinal and transverse) %	≥700
Right angle tearing load (longitudinal and transverse) N	≥93	≥125	≥160	≥190	≥250	≥315	≥375
puncture strength N	≥240	≥320	≥400	≥480	≥640	≥800	≥960
Stress cracking under tensile load		≥300
Carbon black content %	2.0~3.0
Carbon Black Dispersibility	No more than 1 out of 10 data at level 3, not allowed at levels 4 and 5
Atmospheric pressure oxidation induction time (OIT)min	Atmospheric pressure oxidation induction time ≥ 100
Atmospheric pressure oxidation induction time (OIT)min	High pressure oxidation induction time ≥ 400
85°C heat aging %	≥55
anti-ultraviolet	≥50

Glossy HDPE geomembrane for landfill "CJ/T 234-2006 Technical Specification" (equivalent to US GRI-GM13 standard)

Item	Indicator
thicknesses mm	0.75	1.00	1.25	1.50	2.00	2.50	3.00
Densities g/cm³	≥0.939
Tensile yield strength (longitudinal and transverse) N/mm	≥11	≥15	≥18	≥22	≥29	≥37	≥44
Tensile breaking strength (longitudinal and transverse) N/mm	≥20	≥27	≥33	≥40	≥53	≥67	≥80
Yield elongation (longitudinal and transverse) %	≥12
Elongation at break (longitudinal and transverse) %	≥700
Right angle tearing load (longitudinal and transverse) N	≥93	≥125	≥156	≥187	≥249	≥311	≥374
puncture strength N	≥240	≥320	≥400	≥480	≥640	≥800	≥960
Resistant to environmental stress cracking	≥300
Carbon black content %	2.0~3.0
Carbon Black Dispersibility	No more than 1 out of 10 data at level 3, not allowed at levels 4 and 5
Atmospheric pressure oxidation induction time (OIT)min	Atmospheric pressure oxidation induction time ≥ 100
Atmospheric pressure oxidation induction time (OIT)min	High pressure oxidation induction time ≥ 400
85°C heat aging %	≥55
anti-ultraviolet	≥50

FACTORY APPEARANCE

We mainly produce PP bidirectional geogrids, PE and PP unidirectional geogrids, warp knitted geogrids, glass fiber geogrids, basalt geogrids, geotextiles, geomembranes, geonets, safety fences, three-dimensional geogrid mats, geocomposite products, etc.

Shandong Zhonghuan Engineering Materials Co., Ltd.

HONOR

The products are mainly used in the infrastructure construction of roads, railways, irrigation projects, electricity, soil and water conservation and environmental greening.

FAQ

Q: Can we take some samples? Any fees?

A: Yes, we can provide samples free of charge, but we don't pay for shipping. If you place an order after confirming the sample, we will refund your delivery fee or deduct it from the order amount.

Q:Can you deliver the goods on time?

A: Yes, we guarantee the best quality products and punctual delivery. Integrity is the tenet of our company.

Q: What are the loading ports?

A: In general, we ship the goods from Shanghai, Tianjin, Qingdao and Ningbo ports. You can designate other ports according to your needs.

Q: Is there quality inspection before loading?

A: Of course, all our products go through strict quality inspection before packing. Those that fail will be destroyed. Customers can also entrust a third party to inspect the products before loading.

Q: How is the product packaged?

A: Standard export seaworthy packing with waterproof paper inside and iron outside, secured by fumigated wooden pallets. It can effectively protect products from corrosion and various climate changes during Marine transportation.

Dam Liner